PROPERTY | UNIT | VALUE / RANGE |
Melting Point | °C | 220 - 225 |
Density | g mL-1 | 1.30 |
Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | 10.8 - 14.4 |
Heat Deflection Temperature, 0.5 MPa | °C | 50 - 73 |
Heat Deflection Temperature, 1.8 MPa | °C | 115 - 184 |
Thermal Conductivity | W / mK | 0.17 - 0.23 |
Rockwell Hardness, M/R Scale | n/a | R95 - R125 |
PROPERTY | UNIT | VALUE / RANGE |
Tensile Strength, Yield at 23 C | MPa | 58 - 60 |
Tensile Strength, Break at 23 C | MPa | 34 - 60 |
Elongation, Yield | % | 4 - 10 |
Elongation, Break | % | 5 - 8 |
Tensile Modulus at 23 C | MPa | 1600 - 2700 |
Flexural Strength, Yield | MPa | 50 - 85 |
Flexural Modulus | MPa | 1600 - 2400 |
Compressive Strength | MPa | |
Izod Notched | J / m | 3.5 - 90 |
Izod Unnotched | J / m | 3.5 - 4.0 |
PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | > 1013 | |
Dielectric Strength | V/mm x 104 | 2.6 - 3.2 | |
Dielectric Constant @ 1 MHz | n/a | 3.2 | |
Dissipation Factor @ 1 MHz | n/a, x 10-4 | 200 |
PROPERTY | UNIT | VALUE / RANGE | |
| °C | 205 - 275 | |
Mold Shrinkage | % | 0.001 - 0.004 | |
Continuous Service Temperature | °C | 52 - 84 | |
Water Absorption, 24 hr. Immersion | % | 0.4 |